WELDING PROCESSES:

WELDING PROCESSES Arc Welding Resistance Welding Oxyfuel Gas Welding Other Fusion Welding Processes Solid State Welding Weld Quality Weldability Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Two Categories of Welding Processes :

Two Categories of Welding Processes Fusion welding - coalescence is accomplished by melting the two parts to be joined, in some cases adding filler metal to the joint Examples: arc welding, resistance spot welding, oxyfuel gas welding Solid state welding - heat and/or pressure are used to achieve coalescence, but no melting of base metals occurs and no filler metal is added Examples: forge welding, diffusion welding, friction welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Arc Welding (AW):

Arc Welding (AW) A fusion welding process in which coalescence of the metals is achieved by the heat from an electric arc between an electrode and the work Electric energy from the arc produces temperatures ~ 10,000 F (5500 C), hot enough to melt any metal Most AW processes add filler metal to increase volume and strength of weld joint Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

What is an Electric Arc?:

What is an Electric Arc? An electric arc is a discharge of electric current across a gap in a circuit It is sustained by an ionized column of gas ( plasma ) through which the current flows To initiate the arc in AW, electrode is brought into contact with work and then quickly separated from it by a short distance Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

A pool of molten metal is formed near electrode tip, and as electrode is moved along joint, molten weld pool solidifies in its wake Figure 31.1 Basic configuration of an arc welding process. Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Two Basic Types of AW Electrodes:

Two Basic Types of AW Electrodes Consumable – consumed during welding process Source of filler metal in arc welding Nonconsumable – not consumed during welding process Filler metal must be added separately Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Consumable Electrodes :

Consumable Electrodes Forms of consumable electrodes Welding rods (a.k.a. sticks) are 9 to 18 inches and 3/8 inch or less in diameter and must be changed frequently Weld wire can be continuously fed from spools with long lengths of wire, avoiding frequent interruptions In both rod and wire forms, electrode is consumed by arc and added to weld joint as filler metal Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Nonconsumable Electrodes :

Nonconsumable Electrodes Made of tungsten which resists melting Gradually depleted during welding (vaporization is principal mechanism) Any filler metal must be supplied by a separate wire fed into weld pool Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Arc Shielding:

Arc Shielding At high temperatures in AW, metals are chemically reactive to oxygen, nitrogen, and hydrogen in air Mechanical properties of joint can be seriously degraded by these reactions To protect operation, arc must be shielded from surrounding air in AW processes Arc shielding is accomplished by: Shielding gases, e.g., argon, helium, CO 2 Flux Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Flux:

Flux A substance that prevents formation of oxides and other contaminants in welding, or dissolves them and facilitates removal Provides protective atmosphere for welding Stabilizes arc Reduces spattering Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Various Flux Application Methods:

Various Flux Application Methods Pouring granular flux onto welding operation Stick electrode coated with flux material that melts during welding to cover operation Tubular electrodes in which flux is contained in the core and released as electrode is consumed Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Power Source in Arc Welding:

Power Source in Arc Welding Direct current (DC) vs. Alternating current (AC) AC machines less expensive to purchase and operate, but generally restricted to ferrous metals DC equipment can be used on all metals and is generally noted for better arc control Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Consumable Electrode AW Processes :

Consumable Electrode AW Processes Shielded Metal Arc Welding Gas Metal Arc Welding Flux‑Cored Arc Welding Electrogas Welding Submerged Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Shielded Metal Arc Welding (SMAW):

Shielded Metal Arc Welding (SMAW) Uses a consumable electrode consisting of a filler metal rod coated with chemicals that provide flux and shielding Sometimes called "stick welding" Power supply, connecting cables, and electrode holder available for a few thousand dollars Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.3 Shielded metal arc welding (SMAW). Shielded Metal Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.2 Shielded metal arc welding (stick welding) performed by a (human) welder (photo courtesy of Hobart Brothers Co.). Shielded Metal Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

SMAW Applications:

SMAW Applications Used for steels, stainless steels, cast irons, and certain nonferrous alloys Not used or rarely used for aluminum and its alloys, copper alloys, and titanium Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Gas Metal Arc Welding (GMAW):

Gas Metal Arc Welding (GMAW) Uses a consumable bare metal wire as electrode and shielding accomplished by flooding arc with a gas Wire is fed continuously and automatically from a spool through the welding gun Shielding gases include inert gases such as argon and helium for aluminum welding, and active gases such as CO 2 for steel welding Bare electrode wire plus shielding gases eliminate slag on weld bead - no need for manual grinding and cleaning of slag Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.4 Gas metal arc welding (GMAW). Gas Metal Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

GMAW Advantages over SMAW:

GMAW Advantages over SMAW Better arc time because of continuous wire electrode Sticks must be periodically changed in SMAW Better use of electrode filler metal than SMAW End of stick cannot be used in SMAW Higher deposition rates Eliminates problem of slag removal Can be readily automated Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Flux‑Cored Arc Welding (FCAW):

Flux‑Cored Arc Welding (FCAW) Adaptation of shielded metal arc welding, to overcome limitations of stick electrodes Electrode is a continuous consumable tubing (in coils) containing flux and other ingredients (e.g., alloying elements) in its core Two versions: Self‑shielded FCAW - core includes compounds that produce shielding gases Gas‑shielded FCAW - uses externally applied shielding gases Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.6 Flux‑cored arc welding. Presence or absence of externally supplied shielding gas distinguishes the two types: (1) self‑shielded, in which core provides ingredients for shielding, and (2) gas‑shielded, which uses external shielding gases. Flux-Cored Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Electrogas Welding (EGW):

Electrogas Welding (EGW) Uses a continuous consumable electrode, either flux‑cored wire or bare wire with externally supplied shielding gases, and molding shoes to contain molten metal When flux‑cored electrode wire is used and no external gases are supplied, then special case of self‑shielded FCAW When a bare electrode wire used with shielding gases from external source, then special case of GMAW Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.7 Electrogas welding using flux‑cored electrode wire: (a) front view with molding shoe removed for clarity, and (b) side view showing molding shoes on both sides. Electrogas Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Submerged Arc Welding (SAW):

Submerged Arc Welding (SAW) Uses a continuous, consumable bare wire electrode, with arc shielding provided by a cover of granular flux Electrode wire is fed automatically from a coil Flux introduced into joint slightly ahead of arc by gravity from a hopper Completely submerges operation, preventing sparks, spatter, and radiation Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.8 Submerged arc welding. Submerged Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

SAW Applications and Products:

SAW Applications and Products Steel fabrication of structural shapes (e.g., I‑beams) Seams for large diameter pipes, tanks, and pressure vessels Welded components for heavy machinery Most steels (except hi C steel) Not good for nonferrous metals Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Non-consumable Electrode Processes :

Non-consumable Electrode Processes Gas Tungsten Arc Welding Plasma Arc Welding Carbon Arc Welding Stud Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Gas Tungsten Arc Welding (GTAW):

Gas Tungsten Arc Welding (GTAW) Uses a non-consumable tungsten electrode and an inert gas for arc shielding Melting point of tungsten = 3410  C (6170  F) A.k.a. Tungsten Inert Gas (TIG) welding In Europe, called "WIG welding" Used with or without a filler metal When filler metal used, it is added to weld pool from separate rod or wire Applications: aluminum and stainless steel most common Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.9 Gas tungsten arc welding. Gas Tungsten Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Advantages / Disadvantages of GTAW:

Advantages / Disadvantages of GTAW Advantages: High quality welds for suitable applications No spatter because no filler metal through arc Little or no post-weld cleaning because no flux Disadvantages: Generally slower and more costly than consumable electrode AW processes Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Plasma Arc Welding (PAW):

Plasma Arc Welding (PAW) Special form of GTAW in which a constricted plasma arc is directed at weld area Tungsten electrode is contained in a nozzle that focuses a high velocity stream of inert gas (argon) into arc region to form a high velocity, intensely hot plasma arc stream Temperatures in PAW reach 28,000  C (50,000  F), due to constriction of arc, producing a plasma jet of small diameter and very high energy density Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.10 Plasma arc welding (PAW). Plasma Arc Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Advantages / Disadvantages of PAW :

Advantages / Disadvantages of PAW Advantages: Good arc stability Better penetration control than other AW High travel speeds Excellent weld quality Can be used to weld almost any metals Disadvantages: High equipment cost Larger torch size than other AW Tends to restrict access in some joints Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Resistance Welding (RW):

Resistance Welding (RW) A group of fusion welding processes that use a combination of heat and pressure to accomplish coalescence Heat generated by electrical resistance to current flow at junction to be welded Principal RW process is resistance spot welding (RSW) Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.12 Resistance welding, showing the components in spot welding, the main process in the RW group. Resistance Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Components in Resistance Spot Welding:

Components in Resistance Spot Welding Parts to be welded (usually sheet metal) Two opposing electrodes Means of applying pressure to squeeze parts between electrodes Power supply from which a controlled current can be applied for a specified time duration Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Advantages / Drawbacks of RW:

Advantages / Drawbacks of RW Advantages: No filler metal required High production rates possible Lends itself to mechanization and automation Lower operator skill level than for arc welding Good repeatability and reliability Disadvantages: High initial equipment cost Limited to lap joints for most RW processes Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Resistance Spot Welding (RSW):

Resistance Spot Welding (RSW) Resistance welding process in which fusion of faying surfaces of a lap joint is achieved at one location by opposing electrodes Used to join sheet metal parts using a series of spot welds Widely used in mass production of automobiles, appliances, metal furniture, and other products made of sheet metal Typical car body has ~ 10,000 spot welds Annual production of automobiles in the world is measured in tens of millions of units Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.13 (a) Spot welding cycle, (b) plot of squeezing force & current in cycle (1) parts inserted between electrodes, (2) electrodes close, force applied, (3) current on, (4) current off, (5) electrodes opened. Spot Welding Cycle Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Resistance Seam Welding (RSEW):

Resistance Seam Welding (RSEW) Uses rotating wheel electrodes to produce a series of overlapping spot welds along lap joint Can produce air‑tight joints Applications: Gasoline tanks Automobile mufflers Various other sheet metal containers Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.15 Resistance seam welding (RSEW). Resistance Seam Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Resistance Projection Welding (RPW):

Resistance Projection Welding (RPW) A resistance welding process in which coalescence occurs at one or more small contact points on parts Contact points determined by design of parts to be joined May consist of projections, embossments, or localized intersections of parts Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.17 Resistance projection welding (RPW): (1) start of operation, contact between parts is at projections; (2) when current is applied, weld nuggets similar to spot welding are formed at the projections. Resistance Projection Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Oxyfuel Gas Welding (OFW):

Oxyfuel Gas Welding (OFW) Group of fusion welding operations that burn various fuels mixed with oxygen OFW employs several types of gases, which is the primary distinction among the members of this group Oxyfuel gas is also used in flame cutting torches to cut and separate metal plates and other parts Most important OFW process is oxyacetylene welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Oxyacetylene Welding (OAW):

Oxyacetylene Welding (OAW) Fusion welding performed by a high temperature flame from combustion of acetylene and oxygen Flame is directed by a welding torch Filler metal is sometimes added Composition must be similar to base metal Filler rod often coated with flux to clean surfaces and prevent oxidation Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.21 A typical oxyacetylene welding operation (OAW). Oxyacetylene Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Acetylene (C2H2) :

Acetylene (C 2 H 2 ) Most popular fuel among OFW group because it is capable of higher temperatures than any other ‑ up to 3480  C (6300  F) Two stage chemical reaction of acetylene and oxygen: First stage reaction (inner cone of flame): C 2 H 2 + O 2  2CO + H 2 + heat Second stage reaction (outer envelope): 2CO + H 2 + 1.5O 2  2CO 2 + H 2 O + heat Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Maximum temperature reached at tip of inner cone, while outer envelope spreads out and shields work surfaces from atmosphere Figure 31.22 The neutral flame from an oxyacetylene torch indicating temperatures achieved. Oxyacetylene Torch Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Alternative Gases for OFW :

Alternative Gases for OFW Methylacetylene‑Propadiene (MAPP) Hydrogen Propylene Propane Natural Gas Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Other Fusion Welding Processes :

Other Fusion Welding Processes FW processes that cannot be classified as arc, resistance, or oxyfuel welding Use unique technologies to develop heat for melting Applications are typically unique Processes include: Electron beam welding Laser beam welding Electroslag welding Thermit welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Electron Beam Welding (EBW):

Electron Beam Welding (EBW) Fusion welding process in which heat for welding is provided by a highly‑focused, high‑intensity stream of electrons striking work surface Electron beam gun operates at: High voltage (e.g., 10 to 150 kV typical) to accelerate electrons Beam currents are low (measured in milliamps) Power in EBW not exceptional, but power density is Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

EBW Advantages / Disadvantages :

EBW Advantages / Disadvantages Advantages: High‑quality welds, deep and narrow profiles Limited heat affected zone, low thermal distortion High welding speeds No flux or shielding gases needed Disadvantages: High equipment cost Precise joint preparation & alignment required Vacuum chamber required Safety concern: EBW generates x‑rays Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Laser Beam Welding (LBW):

Laser Beam Welding (LBW) Fusion welding process in which coalescence is achieved by energy of a highly concentrated, coherent light beam focused on joint Laser = "light amplification by stimulated emission of radiation" LBW normally performed with shielding gases to prevent oxidation Filler metal not usually added High power density in small area, so LBW often used for small parts Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Comparison: LBW vs. EBW:

Comparison: LBW vs. EBW No vacuum chamber required for LBW No x‑rays emitted in LBW Laser beams can be focused and directed by optical lenses and mirrors LBW not capable of the deep welds and high depth‑to‑width ratios of EBW Maximum LBW depth = ~ 19 mm (3/4 in), whereas EBW depths = 50 mm (2 in) Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Thermit Welding (TW):

Thermit Welding (TW) FW process in which heat for coalescence is produced by superheated molten metal from the chemical reaction of thermite Thermite = mixture of Al and Fe 3 O 4 fine powders that produce an exothermic reaction when ignited Also used for incendiary bombs Filler metal obtained from liquid metal Process used for joining, but has more in common with casting than welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.25 Thermit welding: (1) Thermit ignited; (2) crucible tapped, superheated metal flows into mold; (3) metal solidifies to produce weld joint. Thermit Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

TW Applications:

TW Applications Joining of railroad rails Repair of cracks in large steel castings and forgings Weld surface is often smooth enough that no finishing is required Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Solid State Welding (SSW):

Solid State Welding (SSW) Coalescence of part surfaces is achieved by: Pressure alone, or Heat and pressure If both heat and pressure are used, heat is not enough to melt work surfaces For some SSW processes, time is also a factor No filler metal is added Each SSW process has its own way of creating a bond at the faying surfaces Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Success Factors in SSW:

Success Factors in SSW Essential factors for a successful solid state weld are that the two faying surfaces must be: Very clean In very close physical contact with each other to permit atomic bonding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

SSW Advantages over FW Processes:

SSW Advantages over FW Processes If no melting, then no heat affected zone, so metal around joint retains original properties Many SSW processes produce welded joints that bond the entire contact interface between two parts rather than at distinct spots or seams Some SSW processes can be used to bond dissimilar metals, without concerns about relative melting points, thermal expansions, and other problems that arise in FW Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Solid State Welding Processes:

Solid State Welding Processes Forge welding Cold welding Roll welding Hot pressure welding Diffusion welding Explosion welding Friction welding Ultrasonic welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Forge Welding:

Forge Welding Welding process in which components to be joined are heated to hot working temperature range and then forged together by hammering or similar means Historic significance in development of manufacturing technology Process dates from about 1000 B.C., when blacksmiths learned to weld two pieces of metal Of minor commercial importance today except for its variants Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Roll Welding (ROW):

Roll Welding (ROW) SSW process in which pressure sufficient to cause coalescence is applied by means of rolls, either with or without external heat Variation of either forge welding or cold welding, depending on whether heating of workparts is done prior to process If no external heat, called cold roll welding If heat is supplied, hot roll welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.26 Roll welding (ROW) . Roll Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Roll Welding Applications :

Roll Welding Applications Cladding stainless steel to mild or low alloy steel for corrosion resistance Bimetallic strips for measuring temperature "Sandwich" coins for U.S mint Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Diffusion Welding (DFW):

Diffusion Welding (DFW) SSW process uses heat and pressure, usually in a controlled atmosphere, with sufficient time for diffusion and coalescence to occur Temperatures  0.5 T m Plastic deformation at surfaces is minimal Primary coalescence mechanism is solid state diffusion Limitation: time required for diffusion can range from seconds to hours Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

DFW Applications:

DFW Applications Joining of high‑strength and refractory metals in aerospace and nuclear industries Can be used to join either similar and dissimilar metals For joining dissimilar metals, a filler layer of different metal is often sandwiched between base metals to promote diffusion Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Explosion Welding (EXW):

Explosion Welding (EXW) SSW process in which rapid coalescence of two metallic surfaces is caused by the energy of a detonated explosive No filler metal used No external heat applied No diffusion occurs - time is too short Bonding is metallurgical, combined with mechanical interlocking that results from a rippled or wavy interface between the metals Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Commonly used to bond two dissimilar metals, in particular to clad one metal on top of a base metal over large areas Figure 31.27 Explosive welding (EXW): (1) setup in the parallel configuration, and (2) during detonation of the explosive charge. Explosive Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Friction Welding (FRW):

Friction Welding (FRW) SSW process in which coalescence is achieved by frictional heat combined with pressure When properly carried out, no melting occurs at faying surfaces No filler metal, flux, or shielding gases normally used Process yields a narrow HAZ Can be used to join dissimilar metals Widely used commercial process, amenable to automation and mass production Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.28 Friction welding (FRW): (1) rotating part, no contact; (2) parts brought into contact to generate friction heat; (3) rotation stopped and axial pressure applied; and (4) weld created. Friction Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Applications / Limitations of FRW:

Applications / Limitations of FRW Applications: Shafts and tubular parts Industries: automotive, aircraft, farm equipment, petroleum and natural gas Limitations: At least one of the parts must be rotational Flash must usually be removed Upsetting reduces the part lengths (which must be taken into consideration in product design) Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Ultrasonic Welding (USW):

Ultrasonic Welding (USW) Two components are held together, oscillatory shear stresses of ultrasonic frequency are applied to interface to cause coalescence Oscillatory motion breaks down any surface films to allow intimate contact and strong metallurgical bonding between surfaces Although heating of surfaces occurs, temperatures are well below T m No filler metals, fluxes, or shielding gases Generally limited to lap joints on soft materials such as aluminum and copper Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

PowerPoint Presentation:

Figure 31.29 Ultrasonic welding (USW): (a) general setup for a lap joint; and (b) close‑up of weld area. Ultrasonic Welding Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

USW Applications:

USW Applications Wire terminations and splicing in electrical and electronics industry Eliminates need for soldering Assembly of aluminum sheet metal panels Welding of tubes to sheets in solar panels Assembly of small parts in automotive industry Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320

Weldability:

Weldability Capacity of a metal or combination of metals to be welded into a suitably designed structure, and for the resulting weld joint(s) to possess the required metallurgical properties to perform satisfactorily in intended service Good weldability characterized by: Ease with which welding process is accomplished Absence of weld defects Acceptable strength, ductility, and toughness in welded joint Rattandeep singh (Mechanical engg.)Email:-rsrattanvirdi@gmail.com contact no 9876866320